Antioxidants of steel slab hot rolling For 9%Ni steel plate

Antioxidants of steel slab hot rolling For 9%Ni steel plate

Price: inquiry
Starting quantity: ≥1KGS
keywords: nickle based steel
Steel grades used: X7Ni9;06Ni9DR
order
Description

  HF-9Ni-3 coatings are made of non-metallic inert materials with high temperature resistance. It can effectively reduce the oxidation burning loss and increase the yield of the 9%Ni steel slab. It is able to avoid the grind process and increase surface quality of high temperature 9%Ni steel slab in the process of high temperature heating and hot rolling.The conclusion is our product can significantly reduce your cost!

  For more data of on-site production, send E-mail to:gabrielcheng@haungfucn.com

001

The effect is very obvious without coating protection and after protection.

  Scaling and oxidation of steel during hot rolling causes direct mass loss of steel and serious quality  problems  of  the surface layer. Also,scale, if not  removed on time and rolled-in during hot rolling,can cause surface defects and in some instance even result in scrapping of product. Mill scale must be removed by  high-pressure  water  jetting, pickling, abrasive  blasting, removing  the  top layer, etc., Thus greatly increasing the number ofproduction processes and energy consumption. Furthemore,during heating process  scales  can fall down  to the  bottom of  the  surface and not only damage the furnace and reduce its life,but to remove them it is also necessary to add hard manual labor;wet deslagging method increases energy consumtion.

  The use of  high-temperature  antionxidant  for  steel in production process greatly improves  efficiency, directly  increases  yield  and  quality of steel. At  the  same time reduction of scaling and oxidation simplifies the production process, significantly reduceenergy consumption and allows full use of iron ore and thereby increases production efficiency.

  The mechanism of action of the high temperature steel antioxidant

  The main components of the antionxidant at high temperature steel as metal and non-metal oxides with high resistance temperatures and antioxidant properties.The most commonly used as a suspension sprayed.Individual components make up a suspension. It is sprayed AIeno painted with the metal surface to form a thick layer of approx.0.3mm.after drying thanks adhesive powder in suspension adheres to the metal surface to form a protective layer.

  During heating process, with increasing temperature the slurry protective layer begins to sinter forming a closed and dense solid adhesion layer and thus achieves isolation of oxygen and prevents oxidation and scaling.


  Surface Effect of Steel Billet after Spraying Antioxidant Coatings

  Practical Application of Nano-silicate Antioxidant Coatings

  1.Can be directly sprayed on the surface of various types of steel slabs.

  2.Affer spraying the surface of the slab,ingot solidifies after 30 minutes at ambient temperature of 20℃.After spraying,coating doesn't fall off and in sturdy enough to withstand a collision with other ingots.

  3.Special steels surface quality problems.When slab is taken out of the furnace there is a dense,thick oxidized layer on the surface. Conventional methods are unable to completely remove the scale which is then during rolling rolled-in causing cracking.

  4.When slab,ingot is taken out of furnace after heating process,the color of the surface is compact,free of irregularities

  5.After hot rolling,the slab surface is glossy and of consistent color,ruptures and other surface quality problems are solved.

  6.Mass loss during heating process of conventional steel without the use of an antioxidant is about 1-3%,with the application of antioxidant it falls below 0.5%.Mass loss during heating process of stainless and saecial steels without the use of antioxidane is about.0.8 to 3%,with application of antioxidant it falls to 0.01-0.02%.High-temperature antioxidant for steel solved problems with surface quality and losses caused by high temperature oxidation of various types of steel.